Significantly enhanced breakdown field in Ca1-xSrxCu3Ti4O12 ceramics by tailoring donor densities

Significantly enhanced breakdown field of 24.52 kV cm^?1 as well as noteworthy nonlinear coefficient of 8.11 and low dielectric loss of 0.077 were obtained in Ca_0.6Sr_0.4Cu₃Ti₄O₁₂ ceramic. It was proved from impedance spectra that improved breakdown field was attributed to enhanced grain boundary resistance and elevated Schottky barrier height, which was further found resulting from reduced donor densities in C-V measurements. In addition, it was found that the activation energy originated from oxygen vacancies was increased, indicating the generation of oxygen vacancies was suppressed. Since oxygen vacancies acted as donors in depletion layers, it is reasonable to deduce that the reduced donor density was mainly ascribed to the decreased oxygen vacancies. In conclusion, maximum integrated action of strong solid solution effect and weak Sr-stretching effect was achieved when Sr/Ca ratio is 40/60, leading to greatly elevated potential barrier height and enhanced breakdown field consequently.     

The effects of processing parameters on the morphology of PLA/PEG melt electrospun fibers

Electrospinning of a polymer melt is an ideal technique to produce highly porous nanofibrous or microfibrous scaffolds appropriate for biomedical applications. In recent decades, melt electrospinning has been known as an eco‐friendly procedure as it eliminates the cytotoxic effects of the solvents used in solution electrospinning. In this work, the effects of spinning conditions such as temperature, applied voltage, nozzle to collector distance and collector type as well as polyethylene glycol (PEG) concentration on the diameter of melt electrospun polylactic acid (PLA)/PEG fibers were studied. The thermal stability of PLA/PEG blends was monitored through TGA and rheometry. Morphological investigations were carried out via optical and scanning electron microscopy. Based on the results, blends were almost stable over the temperature range of melt electrospinning (170 ? 230 °C) and a short spinning time of 5 min. To obtain non‐woven meshes with uniform fiber morphologies, experimental parameters were optimized using ANOVA. While increasing the temperature, applied voltage and PEG content resulted in thinner fibers, PEG concentration was the most influential factor on the fiber diameter. In addition, a nozzle to collector distance of 10 cm was found to be the most suitable for preparing uniform non‐woven PLA/PEG meshes. At higher PEG concentrations, alterations in the collector distance did not affect the uniformity of fibers, although at lower distances vigorous bending instabilities due to polarity augmentation and viscosity reduction resulted in curly fibrous meshes. Finally, the finest and submicron scale fibers were obtained through melt electrospinning of PLA/PEG (70/30) blend collected on a metallic frame. © 2017 Society of Chemical Industry     

掺铒单模光纤飞秒脉冲激光器和放大器

为了获得一种被动锁模掺铒光纤振荡器及功率放大器，数值模拟出超短脉冲在光纤中的传输和演化过程，并基于此搭建了一种被动锁模掺铒光纤飞秒振荡器及功率放大器。实验获得了中心波长1560 nm、重复频率100 MHz、输出功率30 mW、脉冲宽度85 fs超短脉冲。通过采用PPLN晶体进行倍频，进一步获得了输出功率5 mW，中心波长780 nm的飞秒脉冲。该光纤激光器为全保偏光纤结构，具有体积小巧、可靠性高、稳定性好的特点。     

Experimental study on the behavior of eccentrically loaded circular footing model resting on reinforced sand

In this study, an experimental investigation has been conducted on a circular footing model subjected to eccentric load resting on the geonet-reinforced sand. To this end, five series of tests were carried out in order to evaluate the effect of reinforcement dimension and eccentricity on the bearing capacity, settlement, and rotation of the footing. Results show that the bearing capacity ratio (BCR) is in direct relationship with eccentricity and the impact of soil reinforcement at low settlements is much more significant in the case of eccentric loading. Additionally, the bearing capacity interaction diagram and variation in the position of rotation line at different load levels for reinforced and unreinforced conditions are presented.     

Review on nano-and microfiller-based polyamide 6 hybrid composite: Effect on mechanical properties and morphology

Polyamide 6 (PA6)-based composites are of evolving interest due to its high strength, wear resistance, and barrier properties. The use of binary composites mostly with nanomaterial and glass fibers has been reviewed and presented in literature. However to obtain a balance of properties like stiffness, toughness, and strength along with cost reduction, ternary composites of PA6 have been designed. To achieve the balance, PA6 blend-based composites, with combination of microfiller/nanofiller or PA6 with combination micro-microfiller, PA6 with microfiller/nanofiller and fiber have been designed. The properties of PA6-based ternary hybrid composites depend on type of dispersed phase used, presence of compatibilizer, type of filler used (nanofiller or microfiller or fiber or hybrid) and combination of fillers used. However, a review in this direction is not available in literature. Here, in this study, an overall understanding of various fillers, dispersed phase, and their combinations can be understood along with the discussion on effect of these on tensile properties and morphology of hybrid composite. In this study, an attempt has been made to review the various fillers and dispersed phase and their combinations which have been used in designing the PA6 hybrid composite with good balance of stiffness, toughness, and strength.     

直纺亮光抗倒伏波浪扁平涤纶FDY的开发

探讨了直纺83 dtex/114 f波浪扁平涤纶全拉伸丝(FDY)的工艺制备过程。试验证明,在熔体输送温度276~282℃,纺丝温度286~290℃,喷丝板规格DIO φ104 mm-114孔、"王"字形,环吹风压10~15 Pa,含油率1.1%~1.2%,卷绕速度3 800~4 200 m/min的工艺参数下纺制83 dtex/114 f波浪扁平涤纶FDY时,生产稳定,满卷率高,外观情况良好,袜带均匀亮丽,可批量生产。此新产品可用于制作高档布艺沙发表层面料,具有抗倒伏、色彩艳丽等功效。     

凉感纤维织物导热系数影响因素的探讨

采用普通涤纶、含1%云母颗粒的涤纶(1%云母/涤纶)以及含5%云母颗粒的涤纶(5%云母/涤纶)三种材质,上机纬密采用200根/10 cm、300根/10 cm、400根/10 cm,组织采用平纹、斜纹、缎纹试织试样。通过Hot Disk热常数分析仪,采用正交试验及极差、方差分析,研究了纤维材质、上机纬密、组织对凉感纤维织物导热系数的影响。结果表明:在试验设置变量范围内,纤维材质对导热系数的影响显著,上机纬密、组织对导热系数的影响高度显著,影响因素从大到小顺序为上机纬密>组织>纤维材质。     

Effects of short carbon fiber on the macro-properties,mechanical performance and microstructure of SiSiC composite fabricated by selective laser sintering

Selective laser sintering was combined with reactive melt infiltration to fabricate SiSiC part, and the effects of carbon fiber (C_f) on the properties of the SLS green body, the carbonized and final SiSiC sample were investigated. Results show that the addition of an appropriate amount of C_f (1.59 wt%~2.97 wt%) can increase the bulk density and geometric precision of the sample at all stages, and improve the mechanical properties of green and carbonized samples. The main phases composed of the SiSiC composite were free Si, a-SiC, β-SiC, plus a very small amount of Al–Si alloy. With 1.59 wt% C_f addition, a relatively comprehensive favorable macro-properties of both the green sample and carbonized sample was achieved, and the homogeneous microstructure of the latter favored the decreased free Si content and increased β-SiC content of the final composite. The evolution mechanism of C_f added to the raw material is inferred to be the mutual diffusion of [C] and [Si] that occurred at the C_f/Si melt boundary leading to the formation of the siliconized C_f with relatively large diameter size (24.3 μm) and high aspect ratio (>30). Amorphous C, which derived from the pyrolysis of epoxy resin E12, undergone a dissolution-precipitation mechanism with the formation of fine-grain β-SiC.     

Nature of heterophase inclusions in high-purity optical fiber materials as studied with 3D laser ultramicroscopy

3D laser ultramicroscopy (3D LUM) is intended specially for determining the concentration and size distribution of submicron inclusions in the bulk samples of high-purity materials for visible and IR fiber optics. In this work the 3D LUM technique is shown to be able to identify the nature of individual inclusions detected. The measurement of the light scattered by an inclusion at a varied probe beam wavelength and polarization and at a varied scattered light collection angle makes it possible to determine the inclusion refractive index. The 3D LUM possibilities are illustrated by the example of studying the inclusion nature in the As₂S₃ glass samples prepared by the direct synthesis from elements in a quartz container at elevated temperatures.